A 50 weight percent solution of butylnorbornene (5.0 g, 0.033 mol) was prepared in toluene. Lithium tetrakis(pentafluorophenyl)borate.2.5 Et2O (0.0012 g, 0.0014 mmol) was combined with (allyl)palladiumchloride dimer (100 μl of a 1.4 mmol solution in toluene) and 2,6-di-t-butylpyridine (100 μl of a 2.9 mmol solution in toluene) in toluene and added to the monomer mixture. A polymeric puck formed within 5-10 min at room temperature.

1. additionadded to the monomer mixture
2. customA polymeric puck formed within 5-10 min at room temperature