Butyl Methacrylate → HCID 131724292, compound

Participants

Reaction Conditions

Reaction Steps

Charge 1 was added to a 4-liter stirred stainless steel pressure reactor. The reactor was then pressurized with nitrogen providing a 5 psig pad on the reactor. The agitation on the reactor was set at 500 rpm and the reactor temperature was adjusted to 150° C. Charge 2 was added to the reactor at an addition rate of 36 grams/hour over 2.5 hours. After 15 minutes Charge 3 was added to reactor at the addition rate 1000 grams/hour over 2 hours. During the monomer addition the temperature was maintained at 150° C. at 100 PSI. After charge 2 and charge 3 were in the reactor, the reaction mixture was held for 2 hours. The reactor was then cooled to 25° C., and vented. GC analysis of the reaction mixture showed that all acrylates, methacrylates and styrene were reacted. The reaction mixture was transferred to 5 L flask, and was vacuum-stripped at 125° C. The final solids of the resulting polymer was determined to be 98.63 at 110° C. for one hour. The copolymer had Mn=1960 and Mw/Mn=2.3. The 13C NMR spectrum is consistent with a molar copolymer composition of 17.67% diisobutylene, 37.1% hydroxypropyl acrylate, 16.36% butyl methacrylate, 8.25% styrene, and 20.62% butyl acrylate.

Provenance & Evidence