A styrene-butadiene dispersion was prepared by free-radical polymerization from 6 kg of styrene, 8.4 kg of 1,3-butadiene, 3.6 kg of acrylic acid, 0.41 kg of styrene seed latex dispersion (34% by weight in water, particle size about 30 to 35 nm), 135 g of Texapon® NSO solution (sodium lauryl ether sulfate having on average 2.5 ethylene oxide units; 28% strength by weight in water), 150 g of sodium hydroxide solution (10% strength by weight in water), 110 g of sodium peroxodisulfate and 18.28 kg of water at 82° C. Excess 1,3-butadiene was removed by injecting 2 bar of nitrogen with stirring into the dispersion, which had been cooled to 68° C., releasing the pressure and applying a slight underpressure (750 mbar absolute) and repeating this procedure in automated form about 1500 times. After 4 hours, a dispersion was obtained which had a solids content of 51.3% by weight, a pH of 4.8, and residual monomer contents of 1669 ppm of styrene and 280 ppm of acrylic acid.

1. customExcess 1,3-butadiene was removed
2. customa dispersion was obtained which