In a 300 mL three-necked flask, N-acryloylmorpholine (14.20 g, 0.101 mol), N,N-dimethylacrylamide (DMA, 9.92 g, 0.100 mol), t-amyl alcohol (96.63 g), a polymerization initiator VA-061 (Wako Pure Chemical Industries, Ltd., 0.0310 g, 0.124 mmol), 2-mercaptoethanol (86 μL, 1.23 mmol) were charged, and then equipped with a three-way stop-cock, a reflux condenser tube, a thermometer and a mechanical stirrer. The concentration of the monomer was 20% by weight. After degassing inside the three-necked flask using a vacuum pump and repeating replacement by argon three times, stirring was carried out at 70° C. for 1 hour, followed by temperature rise to 75° C. and further stirring for 4 hours. After completion of the polymerization, the polymerization reaction solution was cooled to room temperature and the solvent was distilled off by an evaporator, and then washed once with each of n-hexane/methanol (=400 mL/30 mL, 500 mL/40 mL, 130 mL/3 mL and 200 mL/7 mL). The solid component was dried overnight by a vacuum drying oven at 60° C. Liquid nitrogen was charged and the solid component was crushed by a spatula, and then dried by a vacuum drying oven at 60° C. for 3 hours. The thus obtained copolymer had a molecular weight of Mn: 4.3 kD, Mw: 17 kD (Mw/Mn=4.1)).

1. customequipped with a three-way
2. customAfter degassing inside the three-necked flask
3. customfollowed by temperature rise to 75° C.
4. stirringfurther stirring for 4 hours
5. customAfter completion of the polymerization
6. customthe polymerization reaction solution
7. distillationthe solvent was distilled off by an evaporator
8. washwashed once with each of n-hexane/methanol (=400 mL/30 mL, 500 mL/40 mL, 130 mL/3 mL and 200 mL/7 mL)
9. customThe solid component was dried overnight by a vacuum
10. customdrying oven at 60° C
11. additionLiquid nitrogen was charged
12. customthe solid component was crushed by a spatula
13. customdried by a vacuum
14. customdrying oven at 60° C. for 3 hours