Dimethyl Sulfoxide → Acrylic acid hydroxyethyl methacrylate

Participants

Reaction Steps

In a 200 mL three-necked flask, 2-hydroxyethyl methacrylate (HEMA, 11.4 g, 0.10 mol), acrylic acid (AA, 7.21 g, 0.10 mol), dimethyl sulfoxide (74.5 g) and a polymerization initiator VA-061 (Wako Pure Chemical Industries, Ltd., 0.016 g, 0.062 mmol) were charged, and then equipped with a three-way stop-cock, a reflux condenser tube, a thermometer and a mechanical stirrer. The concentration of the monomer was 20% by weight. After degassing inside the three-necked flask using a vacuum pump and repeating replacement by argon three times, stirring was carried out at 60° C. for 0.5 hours, followed by temperature rise to 70° C. and further stirring for 6.5 hours. After completion of the polymerization, the polymerization reaction solution was cooled to room temperature, and then the mixed solution was poured into water (1,000 mL)/ethanol (10 mL) and left to stand overnight. On the next day, the supernatant was discarded and the obtained solid component was further washed twice with 700 mL of water. The solid component was dried overnight by a vacuum drying oven at 60° C. Liquid nitrogen was charged and the solid component was crushed by a spatula, and then dried by a vacuum drying oven at 60° C. for 3 hours. The thus obtained copolymer had a molecular weight of Mn: 79 kD, Mw: 226 kD (Mw/Mn=2.9).

Provenance & Evidence