Versuchsvorschrift
A toner was prepared by extrusion with the above polymer, 92 percent, 6 percent of Regal 330® carbon black and 2 percent of CPC (cetyl pyridinium chloride charge additive) followed by micronization to 10 microns. The minimum fix temperature of the toner was 210° F. as determined by no cracking of the fused toner images as a result of a 180° paper crease test (paper folded 180 degrees, visually observed the breadth of cracking at crease) and the minimum fix temperature of the toner was 230° F. when no appreciable, for example a peppered, toned image was removed with SCOTCH® Tape Magic 810, and the hot offset temperature was 320° F. where the toned image sticks to silicone roll fuser as indicated herein. When fused, toner images were observed to offset from paper onto a silicone fuser roll, and then was imprinted onto the same paper or subsequent papers.
Aufarbeitung
- customwas 210° F.
- customa result of a 180° paper crease test (paper folded 180 degrees
- customwas 230° F.
- customwas removed with SCOTCH® Tape Magic 810
- customwas 320° F.
Quellen und Nachweise
- ORD-Eintrag
- ord-a261e920e55243638bd074188a300a17
- Quelldatensatz
- uspto-grants-1994_01
- Patentnummer
- US05278016
Verknüpfte Notizen
Wird geladen…