Reaktionsgleichung
O=[Ce:2]=O.[C:4](=[O:7])([O-])[O-:5].[Ce+3].[C:9](=[O:12])([O-])[O-:10].[C:13](=[O:16])([O-])[O-:14].[Ce+3]>C(O)(=O)C>[C:4]([O-:5])(=[O:7])[CH3:9].[Ce+3:2].[C:9]([O-:10])(=[O:12])[CH3:13].[C:13]([O-:14])(=[O:16])[CH3:4]Komponenten
Reagenzien, Katalysatoren, Lösungsmittel 1
Versuchsvorschrift
High surface area ceria was first prepared following traditional procedures. Five grams of cerium carbonate was slowly mixed with 4.5 ml of glacial acetic acid to produce cerium acetate. The sample was dried in a vacuum over at 100° C., the calcined in air at 425° C. to produce cerium oxide. The ceria was coated with a layer of Al2O3 to act as a template by mixing 2 g of the ceria with 40 ml of a 0.01M Al2O3 sol (diluted from a 20 wt % sol), stirring overnight, then filtering, washing, drying, and calcining in air at 500° C. as above. The zeolite precursor solution was prepared by mixing a solution containing NaOH, dissolved Al foil, and H2O with tetraethylorthosilicate (TEOS) and tetrapropylammonium hydroxide (TPAOH) such that the molar concentrations in the final solution was 4:0.06:571:6:1 NaOH:Al:H2O:TEOS:TPAOH. The solution was stirred at room temperature overnight, then approximately 40 ml was added to 2 g of the Al2O3 coated ceria in an autoclave. The autoclave was heated to 175° C. for 6 hrs under autogenic pressure. After rapid cooling, the sample was filtered, washed, dried, then calcined for 6 hrs in air at 500° C. to remove residual organic compounds. Copper was exchanged with the zeolite film/ceria following the methods listed above for CeO2/Cu-ZSM-5. The final catalyst will be referred to as “Cu-ZSM-5/CeO2”.
Quellen und Nachweise
- ORD-Eintrag
- ord-a8e431e18d1c49b9a2cc767ec26cc9f7
- Quelldatensatz
- uspto-grants-2007_05
- Patentnummer
- US07220692B2
Verknüpfte Notizen
Wird geladen…