Phosphoric Acid → Phosphate cerium nitrate

HRID 1421337

Reaktionsgleichung

Reaktionsgleichung von HRID 1421337
O.O.O=[Al]O[Si](O[Si](O[Al]=O)=O)=O.[P:14](=[O:18])([OH:17])([OH:16])[OH:15].[N+:19]([O-:22])([O-:21])=[O:20].[Ce+3:23].[N+]([O-])([O-])=O.[N+]([O-])([O-])=O.[C:32]([O-:37])(=[O:36])[C:33]([O-:35])=[O:34].[V+5:38].[C:39]([O-:44])(=[O:43])[C:40]([O-:42])=[O:41].[C:45]([O-:50])(=[O:49])[C:46]([O-:48])=[O:47].[C:51]([O-:56])(=[O:55])[C:52]([O-:54])=[O:53].[C:57]([O-:62])(=[O:61])[C:58]([O-:60])=[O:59].[V+5]>O>[P:14]([O-:18])([O-:17])([O-:16])=[O:15].[N+:19]([O-:22])([O-:21])=[O:20].[Ce+3:23].[N+:19]([O-:22])([O-:21])=[O:20].[N+:19]([O-:22])([O-:21])=[O:20].[C:32]([O-:37])(=[O:36])[C:33]([O-:35])=[O:34].[V+5:38].[C:39]([O-:44])(=[O:43])[C:40]([O-:42])=[O:41].[C:45]([O-:50])(=[O:49])[C:46]([O-:48])=[O:47].[C:51]([O-:56])(=[O:55])[C:52]([O-:54])=[O:53].[C:57]([O-:62])(=[O:61])[C:58]([O-:60])=[O:59].[V+5:38]

Komponenten

7

Edukt 4

HCID 1004Phosphoric AcidHCID 24948Cerium nitrateHCID 56841936BentoneHCID 178526029HCID 178526029, Verbindung

Produkt 2

HCID 86755301Phosphate cerium nitrateHCID 178526029HCID 178526029, Verbindung

Reagenzien, Katalysatoren, Lösungsmittel 1

HCID 962WaterLösungsmittel

Versuchsvorschrift

A clay/phosphate/cerium nitrate, vanadium oxalate slurry was prepared by adding 1340 grams of Theile RC-32® kaolin clay slurry to 1795 milliliters of water in a high speed mixer. To this mixture, 192 grams of phosphoric acid was added. Thereafter, 431 grams of cerium nitrate solution and 232 grams of vanadium oxalate solution were added to the slurry. The slurry was then spray dried and then resulting particles were calcined at 650° C. for 30 minutes in a muffle furnace. The calcined particles were then mixed with magnesium oxide in a 50/50 weight percent ratio and analyzed by TGA tests. These tests indicated that the resulting material produced an SOx absorption of 0.27% per minute.

Aufarbeitung

  1. customThe slurry was then spray dried
  2. additionThe calcined particles were then mixed with magnesium oxide in a 50/50 weight percent ratio
  3. customproduced
  4. customan SOx absorption of 0.27% per minute

Quellen und Nachweise

ORD-Eintrag
ord-cb4af3e3c8fb489bb52a91cf4a81a31b
Quelldatensatz
uspto-grants-2000_06
Patentnummer
US06074984

Verknüpfte Notizen