Chloride → Acrylamide

HRID 1598489

Reaktionsgleichung

Reaktionsgleichung von HRID 1598489
[C:1]([NH2:5])(=[O:4])[CH:2]=[CH2:3].[Cl-:6].[C:7]([O:11][CH2:12][CH3:13])(=[O:10])[CH:8]=[CH2:9].C(N(CC(O)=O)CC(O)=O)CN(CC(O)=O)CC(O)=O.Cl.Cl.N(C(C1NCCN=1)(C)C)=NC(C1NCCN=1)(C)C>O>[C:1]([NH2:5])(=[O:4])[CH:2]=[CH2:3].[CH3:7][Cl:6].[C:7]([O:11][CH2:12][CH3:13])(=[O:10])[CH:8]=[CH2:9]

Komponenten

8

Edukt 5

HCID 312ChlorideHCID 6049Ethylenediaminetetraacetic AcidHCID 6579AcrylamideHCID 8821Ethyl AcrylateHCID 99491012,2'-Azobis[2-(2-imidazolin-2-yl)propane] dihydrochloride

Produkt 2

HCID 6579AcrylamideHCID 23497919MeCl EA

Reagenzien, Katalysatoren, Lösungsmittel 1

HCID 962WaterLösungsmittel

Versuchsvorschrift

A 10% solution of poly(AMD/DMAEA.MeCl/EA) was prepared as follows: 13.87 parts of 53.58% aqueous acrylamide (AMD), 25.31 parts of a 80% aqueous solution of ethacryloxyethyltrimethylammonium chloride (DMAEA.MeCl), 2.33 parts of ethyl acrylate (EA), 0.3 part EDTA, 258.16 parts of deionized water and 0.030 parts of VA-044 were added to a suitable glass vessel. The solution was sparged with nitrogen gas and stirred for about one hour at ambient temperature. The nitrogen sparge was changed to a nitrogen purge, and polymerization was initiated thermally by raising the temperature of the solution to 44° C. Stirring and heating were continued for about 21 hours to give a clear, viscous solution of poly(AMD/DMAEA.MeCl/EA) having a standard viscosity of about 2.0 centipoise.

Aufarbeitung

  1. customThe solution was sparged with nitrogen gas
  2. customThe nitrogen sparge
  3. custompurge
  4. custompolymerization
  5. temperatureby raising the temperature of the solution to 44° C
  6. stirringStirring
  7. temperatureheating
  8. waitwere continued for about 21 hours

Quellen und Nachweise