Monobasic potassium phosphate → Magnesium Phosphate

HRID 217543

Reaktionsgleichung

Reaktionsgleichung von HRID 217543
[P:1]([OH:5])([OH:4])([O-:3])=[O:2].[K+].[O-2].[Mg+2:8]>O>[P:1]([O-:5])([O-:4])([O-:3])=[O:2].[Mg+2:8].[P:1]([O-:5])([O-:4])([O-:3])=[O:2].[Mg+2:8].[Mg+2:8]

Komponenten

4

Edukt 2

HCID 516951Monobasic potassium phosphateHCID 6850729Magnesium monoxide

Produkt 1

HCID 24439Magnesium Phosphate

Reagenzien, Katalysatoren, Lösungsmittel 1

HCID 962WaterLösungsmittel

Versuchsvorschrift

This example illustrates that the coating can be applied to organic substrates. A magnesium phosphate coating composition was prepared by combining 60 grams of mono-potassium phosphate crystals (maximum size 300 microns), 20 grams of magnesium oxide powder (maximum size 100 microns), and 50 grams fine sand (maximum size 500 microns). The components were blended in high shear mixer for 1 minute and allowed to cool for 10 minutes. Water in the amount of 35 grams was added to this mixture. The components were then mixed by hand in a container to obtain a slurry. This slurry was applied to an asphalt surface using a brush and allowed to cure for about an hour. Once the slurry coating dried, the coating of Example 3 was applied.

Aufarbeitung

  1. temperatureto cool for 10 minutes
  2. additionThe components were then mixed by hand in a container
  3. customto obtain a slurry
  4. waitto cure for about an hour
  5. customOnce the slurry coating dried

Quellen und Nachweise

ORD-Eintrag
ord-053196cc9c874c5798b85b86f4fb8ec4
Quelldatensatz
uspto-grants-2012_06
Patentnummer
US08197593B2