The prepared substrate was next painted with a n-butanol solution containing salts of iridium and tantalum. The ratio of iridium to tantalum in the solution was approximately 65% to 35% by weight. The solution was allowed to dry at ambient temperature for approximately 20 minutes. The painted titanium substrate was subsequently heat treated in a furnace having an oxygen containing atmosphere at approximately 500° C. for approximately 20-30 minutes to form an iridium oxide/tantalum oxide composite coating. The process of painting and heat treating the titanium substrate was repeated in order to obtain a first layer having a total loading of approximately 2.0 g/m2. When the desired loading was achieved, the coated substrate was heat treated for approximately one hour at approximately 500° C.
Aufarbeitung
- customto dry at ambient temperature for approximately 20 minutes
- temperatureThe painted titanium substrate was subsequently heat
- additiontreated in a furnace
- customat approximately 500° C.
- customfor approximately 20-30 minutes
Quellen und Nachweise
- ORD-Eintrag
- ord-112b51fb4a4540469b0301fd066a7d32
- Quelldatensatz
- uspto-grants-2001_04
- Patentnummer
- US06217729B1
Verknüpfte Notizen
Wird geladen…