[CH2:1]1[O:8][C:6](=[O:7])[CH2:5][O:4][C:2]1=[O:3].[C:9]1(=[O:16])[O:15][CH2:14][CH2:13][CH2:12][CH2:11][CH2:10]1.CCCCC(C([O-])=O)CC.CCCCC(C([O-])=O)CC.[Sn+2].C(O)CCCCCCCCC.CC1OC(=O)C(C)OC1=O>>[C:9]1(=[O:16])[O:15][CH2:14][CH2:13][CH2:12][CH2:11][CH2:10]1.[CH2:1]1[O:8][C:6](=[O:7])[CH2:5][O:4][C:2]1=[O:3]Glycolide (0.13 moles) was mixed with ε-caprolactone (1.18) and a catalytic amount of stannous octoate (0.262 mole) and 1-decanol (3.275 mole). The system was heated to 170° C. and was stirred at this temperature for 30 minutes. The reaction was then cooled to 120° C. Glycolide (0.65 moles) and dl-lactide (0.52 moles) were added to the prepolymer. After melting the second charge, the system was heated to 170° C. and was stirred at this temperature for 6.5 hours. At the conclusion of the reaction, the unreacted monomer was removed by heating at 130° C. under reduced pressure for 1.5 hours. The resulting polymer was characterized by DSC (for Tm), solution viscosity (for molecular dimensions), IR and NMR (for chemical composition).