Isoprene → Isoprene acrylonitrile
Reaktionsgleichung
[CH2:1]=[CH:2][C:3](=[CH2:5])[CH3:4].Cl[CH:7]([CH3:10])[C:8]#[N:9]>>[CH2:1]=[CH:2][C:3](=[CH2:4])[CH3:5].[C:8](#[N:9])[CH:7]=[CH2:10]Komponenten
3
Reaktionsbedingungen
- Temperatur
- 80 °C
Versuchsvorschrift
Then, were added thereto 68.2 parts of isoprene and 1.79 parts of 2-chloropropionitrile as an organic halide and stirred under heating at 80° C. to conduct a polymerization reaction. After 137 hours, the same post-treatment as in Example 1 was carried out to give a random (isoprene/acrylonitrile) copolymer. The conversion rate of isoprene was 84% and the conversion rate of acrylonitrile was 79%. The analysis results of the random (isoprene/acrylonitrile) polymer obtained are shown in Table 3. The polymer was confirmed to have a chlorine atom at the terminal of the polymer chain.
Aufarbeitung
- additionThen, were added
- custom