[N:1]12[Si:6]34[N:7]5[Si:4]61[N:5]3[Si:2]25[N:3]64.[C-:8]#[Si+:9]>[O-2].[Y+3].[O-2].[O-2].[Y+3].C(O)C>[N:1]12[Si:6]34[N:7]5[Si:4]61[N:5]3[Si:2]25[N:3]64.[C-:8]#[Si+:9].[CH4:8]参加物
実験手順
644 g of a silicon nitride powder (SN-E10 manufactured by Ube Industries, Ltd.; average particle size: 0.3 μm), 276 g of a silicon carbide (beta random ultrafine grade manufactured by Ibiden Co., Ltd.; average particle size: 0.27 μm), 80 g of an yttrium oxide powder (manufactured by Nippon Yttrium Co., Ltd.; average particle size: 1.4 μm) and 1000 g of ethanol as the dispersion medium were blended under pulverizing in a ball mill for 18 hours using 800 g of silicon nitride balls as a tumbling media. The resultant mixture was dried to obtain a starting ceramic powder mixture having a BET specific surface area of 12.1 m2/g. The above amounts, 644 g of silicon nitride and 276 g of silicon carbide, correspond to theoretical amounts of silicon nitride and silicon carbide formed from 578.6 g of silicon and 82.9 g of carbon black used in Example 1.
後処理
- dry with materialThe resultant mixture was dried
- customto obtain a starting ceramic powder mixture
出典と根拠
- ORDレコード
- ord-b1812e34b3d749299f142af3a0559312
- 出典データセット
- uspto-grants-2001_07
- 特許番号
- US06261511B1
関連ノート
読み込み中…