Styrene → Styrene glycidyl Methacrylate

HRID 1904805

反応式

HRID 1904805 の反応式
[CH2:1]=[CH:2][C:3]1[CH:8]=[CH:7][CH:6]=[CH:5][CH:4]=1.[C:9]([O:14][CH2:15][CH:16]1[O:18][CH2:17]1)(=[O:13])[C:10]([CH3:12])=[CH2:11].C(OS(C1C=CC=CC=1)(=O)=O)CCCCCCCCCCC.[Na].[O-]O.C1(C(C)C)C=CC=CC=1.[Cl-].[Ca+2].[Cl-]>O>[CH2:1]=[CH:2][C:3]1[CH:8]=[CH:7][CH:6]=[CH:5][CH:4]=1.[C:9]([O:14][CH2:15][CH:16]1[O:18][CH2:17]1)(=[O:13])[C:10]([CH3:12])=[CH2:11]

参加物

7

反応物 5

HCID 7501StyreneHCID 7837Glycidyl methacrylateHCID 5284359Calcium ChlorideHCID 53627471Cumen hydroperoxideHCID 57371080Sodium dodecylbenzene sulphonate

生成物 1

HCID 21867792Styrene glycidyl Methacrylate

試薬・触媒・溶媒 1

HCID 962Water溶媒

実験手順

A stainless steel reactor equipped with a stirrer was purged with nitrogen. In the reactor were placed, under a nitrogen stream, 45 parts of styrene, 5 parts of glycidyl methacrylate, 0.43 part of tert-dodecylmercaptan, 1.0 part of sodium dodecylbenzenesulfonate and 140 parts of deionized water. While circulating hot water at 70° C. in the jacket of the reactor, there are further added thereto an aqueous solution of 0.1 part of sodium ethylenediaminetetraacetate, 0.003 part of ferrous sulfate, 0.2 part of formaldehyde-sodium sulfoxylate dihydrate and 15 parts of deionized water and 0.3 part of cumene hydroperoxide. Thereafter, polymerization reaction was effected for 2 hours. Subsequently, 45 parts of styrene, 5 parts of glycidyl methacrylate, 0.43 parts of tertdodecylmercaptan, 1.0 part of sodium dodecylbenzenesulfonate, 90 parts of deionized water and 0.3 part of cumene hydroperoxide were added, and the polymerization reaction was effected for a further 3 hours. To the resulting polymer latex was added an aqueous calcium chloride solution to coagulate the talex, and the polymer obtained was then washed, dehydrated and dried to obtain a polymer (Polymer D-1).

後処理

  1. customA stainless steel reactor equipped with a stirrer
  2. customwas purged with nitrogen
  3. customat 70° C.
  4. additionare further added
  5. customThereafter, polymerization reaction
  6. customthe polymerization reaction
  7. waitwas effected for a further 3 hours
  8. customthe polymer obtained
  9. washwas then washed
  10. customdried
  11. customto obtain a polymer (Polymer D-1)

出典と根拠

ORDレコード
ord-0c8b513446e241db8413f950c95868c1
出典データセット
uspto-grants-1989_06
特許番号
US04839425