1-Dodecanol → L-lactide epsilon-caprolactone

HRID 2258

反応式

HRID 2258 の反応式
C(O)CCCCCCCCCCC.[CH3:14][CH2:15][CH2:16][CH2:17][CH:18]([C:21]([O-:23])=[O:22])[CH2:19]C.CCC[CH2:27][CH:28]([C:31]([O-:33])=[O:32])CC.[Sn+2]>>[C:21]1(=[O:23])[O:22][CH2:14][CH2:15][CH2:16][CH2:17][CH2:18]1.[CH3:27][C@@H:28]1[O:23][C:21](=[O:22])[C@H:18]([CH3:19])[O:33][C:31]1=[O:32]

参加物

3

反応物 2

HCID 81931-DodecanolHCID 93182-ethylhexanoic acid tin(II) salt

生成物 1

HCID 131710947L-lactide epsilon-caprolactone

実験手順

The procedure in Example 1 was substantially repeated, except that 13.6 mL of 1-dodecanol instead of 4.00 mL of glycerol and 0.12 mL (40 μmol) instead of 0.10 mL of stannous octoate solution were used. The copolymer was dried under vacuum (0.1mm Hg) at 110° C. for about 16 hours to remove any unreacted monomer. The copolymer had an inherent viscosity of 0.15 dL/g in HFIP at 25° C. The copolymer was viscous liquid at room temperature. The molar ratio of PC.L/PLA was found to be 51.5/48.5 by proton NMR.

後処理

  1. customThe copolymer was dried under vacuum (0.1mm Hg) at 110° C. for about 16 hours
  2. customto remove any unreacted monomer
  3. customat 25° C
  4. customat room temperature