4-Hydroxybenzoic Acid → 2-Naphthalenecarboxylic acid, 6-(acetyloxy)-, polymer with 4-(acetyloxy)benzoic acid
反応式
[OH:1][C:2]1[CH:10]=[CH:9][C:5]([C:6]([OH:8])=[O:7])=[CH:4][CH:3]=1.[OH:11][C:12]1[CH:13]=[C:14]2[C:19](=[CH:20][CH:21]=1)[CH:18]=[C:17]([C:22]([OH:24])=[O:23])[CH:16]=[CH:15]2.O=[Sb]O[Sb]=O>>[OH:11][C:12]1[CH:13]=[C:14]2[C:19](=[CH:20][CH:21]=1)[CH:18]=[C:17]([C:22]([OH:24])=[O:23])[CH:16]=[CH:15]2.[OH:1][C:2]1[CH:10]=[CH:9][C:5]([C:6]([OH:8])=[O:7])=[CH:4][CH:3]=1参加物
4
実験手順
Charging was conducted at a ratio of 0.6 mol of parahydroxybenzoic acid (PHBA) per mol of 6-hydroxy-2-naphthoic acid (HNCA), 110 ppm of a catalyst in the form of antimony trioxide was added based on the number of mols of HNCA, and the mixture was reacted for 4 hours at 300° C. under reduced pressure. Strands of molten polymer were extruded from the outlet, cooled, and cut to obtain HNCA+PHBA pellets.