反応式
[O-2].[Cd+2:2].[CH2:3]([C:17]([OH:19])=[O:18])[CH2:4][CH2:5][CH2:6][CH2:7][CH2:8][CH2:9][CH2:10][CH2:11][CH2:12][CH2:13][CH2:14][CH2:15][CH3:16]>>[CH2:3]([C:17]([O-:19])=[O:18])[CH2:4][CH2:5][CH2:6][CH2:7][CH2:8][CH2:9][CH2:10][CH2:11][CH2:12][CH2:13][CH2:14][CH2:15][CH3:16].[Cd+2:2].[CH2:3]([C:17]([O-:19])=[O:18])[CH2:4][CH2:5][CH2:6][CH2:7][CH2:8][CH2:9][CH2:10][CH2:11][CH2:12][CH2:13][CH2:14][CH2:15][CH3:16]参加物
反応条件
- 温度
- 90 °C
実験手順
Cadmium oxide (0.127 g, 1 mmol) and tetradecylcarboxylic acid (0.500 g) were reacted at 220° C. for 10 min, cooled to 90° C., then a cadmium tetradecylcarboxylate (precursor) was formed. Into said system, toluene (10 ml), dodecyl mercaptan (1.2 ml) and tetraoctylammonium bromide (0.546 g, as a phase-transfer catalyst) and trioctylphosphine (3.7 g) were added. Then a 0.05M aqueous solution of sodium hydrogen selenide (10 ml) was added. After the system was reacted at 90° C. for 3 h, a red sol containing the dodecyl mercaptan-coated CdSe nanoparticles was obtained. The sol has a typical exciton absorption peak of the ZnSe nanoparticles, can result in a quantum size effect and emit a fairly strong green light under the irradiation of a UV lamp.
出典と根拠
- ORDレコード
- ord-e1bd9a7b5f154593802a68f663571225
- 出典データセット
- uspto-grants-2009_09
- 特許番号
- US07582543B2
関連ノート
読み込み中…