Isobutylene → N-phenylmaleimide isobutene

HRID 891180

反応式

HRID 891180 の反応式
C([O-])(=O)CCCC[CH2:6][C:7](C)([CH3:9])[CH3:8].[C:13]1([N:19]2[C:23](=[O:24])[CH:22]=[CH:21][C:20]2=[O:25])[CH:18]=[CH:17][CH:16]=[CH:15][CH:14]=1.C=C(C)C>C1(C)C=CC=CC=1>[C:13]1([N:19]2[C:23](=[O:24])[CH:22]=[CH:21][C:20]2=[O:25])[CH:14]=[CH:15][CH:16]=[CH:17][CH:18]=1.[CH2:6]=[C:7]([CH3:9])[CH3:8]

参加物

5

反応物 3

HCID 8255IsobutyleneHCID 13662N-PhenylmaleimideHCID 21225528Neodecanoate

生成物 1

HCID 69501867N-phenylmaleimide isobutene

試薬・触媒・溶媒 1

HCID 1140Toluene溶媒

実験手順

In a one-liter autoclave were charged 400 ml of toluene as a polymerization solvent, 0.001 moles of perbutyl neodecanoate as a polymerization initiator, 0.42 moles of N-phenylmaleimide, and 4.05 moles of isobutene, and the mixture was subjected to polymerization reaction under a polymerization condition at a polymerization temperature of 60° C. for a polymerization time of 5 hours, to obtain N-phenylmaleimide-isobutene alternating copolymer. The thus obtained N-phenylmaleimide-isobutene alternating copolymer had a weight average molecular weight (Mw) (as reduced into standard polystyrene) of 162,000 and an Mw/Mn of 2.6.

後処理

  1. customthe mixture was subjected to polymerization reaction under a polymerization condition at a polymerization temperature of 60° C. for a polymerization time of 5 hours

出典と根拠

ORDレコード
ord-7996e10921c24b5780e9d828df5d9dd9
出典データセット
uspto-grants-2006_02
特許番号
US07001967B2