Formaldehyde → Melamine formaldehyde

HRID 1158183

반응식

HRID 1158183 반응식
CCN(C1C=CC2C3(C4C=C(Cl)C=CC=4OC=2C=1)O[C:19](=[O:20])C1C3=CC=CC=1)CC.[OH-].[Na+].[N:32]1[C:39]([NH2:40])=[N:38][C:36]([NH2:37])=[N:35][C:33]=1[NH2:34].C=O>O>[CH2:19]=[O:20].[N:32]1[C:39]([NH2:40])=[N:38][C:36]([NH2:37])=[N:35][C:33]=1[NH2:34]

참가 물질

6

반응물 4

HCID 712FormaldehydeHCID 7955MelamineHCID 14798Sodium Hydroxide2회HCID 117320Spiro[isobenzofuran-1(3H),9'-[9H]xanthen]-3-one, 2'-chloro-6'-(diethylamino)-

생성물 1

HCID 93374Melamine formaldehyde

시약·촉매·용매 1

HCID 962Water용매

반응 조건

온도
60 °C

실험 절차

A solution prepared by dissolving 2.5 parts by weight of 3-diethylamino-7-chlorofluoran in 80 parts by weight of NISSEKI HISOL N-296 (an oil, a trade name, mfd. by Nippon Sekiyu Kagaku K.K.) was emulsified in 100 parts by weight of a 5% aqueous solution of pH 4.0 prepared by dissolving a styrene-maleic anhydride copolymer together with a small amount of sodium hydroxide. On the other hand, when a mixture of 10 parts by weight of melamine, 25 parts by weight of a 37% aqueous formaldehyde solution and 65 parts by weight of water was adjusted to pH 9.0 with sodium hydroxide and heated at 60° C., the mixture became transparent after 15 minutes and a melamine-formaldehyde precondensate was obtained. The precondensate was added to the emulsion obtained above, and the resulting mixture was continuously stirred for 4 hours while maintaining the mixture at 60° C., and then was cooled to room temperature. The solid content of the resulting microcapsule dispersion was 45%.

후처리

  1. customA solution prepared
  2. customprepared

출처 및 근거