Azobisisobutyronitrile → hydroxystyrene (3-acryloxypropyl)trimethylsiloxy Silane

HRID 1355314

반응식

HRID 1355314 반응식
[C:1]([O:5][CH2:6][CH2:7][CH2:8][SiH2:9][O:10][Si:11]([CH3:14])([CH3:13])[CH3:12])(=[O:4])[CH:2]=[CH2:3].C([O:18][CH:19]=[CH:20][C:21]1[CH:26]=[CH:25][CH:24]=[CH:23][CH:22]=1)(=O)C.CC(N=NC(C#N)(C)C)(C#N)C>C1COCC1>[OH:18][CH:19]=[CH:20][C:21]1[CH:26]=[CH:25][CH:24]=[CH:23][CH:22]=1.[C:1]([O:5][CH2:6][CH2:7][CH2:8][SiH2:9][O:10][Si:11]([CH3:14])([CH3:12])[CH3:13])(=[O:4])[CH:2]=[CH2:3]

참가 물질

5

반응물 3

HCID 6547AzobisisobutyronitrileHCID 1145762-Phenylvinyl acetateHCID 131723942(3-Acryloxypropyl)trimethylsiloxy silane

생성물 1

HCID 131723941hydroxystyrene (3-acryloxypropyl)trimethylsiloxy Silane

시약·촉매·용매 1

HCID 8028Tetrahydrofuran용매

반응 조건

온도
65 °C

실험 절차

5 g (3-acryloxypropyl)trimethylsiloxy silane, 38 g acetoxystyrene and 2.41 g AIBN were dissolved in 128 g THF and charged into a 3-neck flask. The system was then purged with N2 for 30 mins before the temperature was raised to 65° C. The reaction was carried out overnight under N2. On the second day, 100 g methanol and 30 mL 30% ammonia hydroxide were added to the system and the temperature was kept at 60° C. The reaction was carried out overnight under N2. On the third day, the solution was precipitated in 2000 mL water and 20 mL acetic acid. The polymer was collected and dried in vacuum oven overnight at 40° C. The molecular weight was determined by gel permeation chromatography (GPC) to be 7.5K.

후처리

  1. additioncharged into a 3-neck flask
  2. customThe system was then purged with N2 for 30 mins before the temperature
  3. additionOn the second day, 100 g methanol and 30 mL 30% ammonia hydroxide were added to the system
  4. customwas kept at 60° C
  5. waitThe reaction was carried out overnight under N2
  6. customOn the third day, the solution was precipitated in 2000 mL water
  7. customThe polymer was collected
  8. customdried in vacuum oven overnight at 40° C