Hexasodium hexametaphosphate → SHP silicate

HRID 1657556

반응식

B([O-])([O-])[O-].B([O-])([O-])[O-].B([O-])([O-])[O-].B([O-])([O-])[O-].B([O-])([O-])[O-].[Na+:21].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[O-:36][P:37]1([O:54][P:52]([O-:55])(=[O:53])[O:51][P:49]([O-:56])(=[O:50])[O:48][P:46]([O-:57])(=[O:47])[O:45][P:43]([O-:58])(=[O:44])[O:42][P:40]([O-:59])(=[O:41])[O:39]1)=[O:38].[Na+].[Na+].[Na+].[Na+].[Na+].[Na+].[Si:66]([O-:70])([O-:69])([O-:68])[O-:67].[Na+].[Na+].[Na+].[Na+]>>[O-:59][P:40]1([O:39][P:37]([O-:38])(=[O:36])[O:54][P:52]([O-:55])(=[O:53])[O:51][P:49]([O-:56])(=[O:50])[O:48][P:46]([O-:57])(=[O:47])[O:45][P:43]([O-:58])(=[O:44])[O:42]1)=[O:41].[Na+:21].[Na+:21].[Na+:21].[Na+:21].[Na+:21].[Na+:21].[Si:66]([O-:70])([O-:69])([O-:68])[O-:67]

참가 물질

반응물 3

HCID 24968Hexasodium hexametaphosphate2회

HCID 26051Sodium orthosilicate

HCID 86741962HCID 86741962, 화합물

생성물 1

HCID 131710291SHP silicate

실험 절차

In the film-forming system that we have found of particular advantage in carrying out our invention comprising a homogeneous solution of sodium silicate and a polysalt, the ratio of a polysalt solids to silicate solids should be between 0.02/1.0 and 3.0/1.0. If a solution of ammonium pentaborate and sodium silicate is used the solids would be 5 to 35% with 3 to 15% ammonium pentaborate (APB) with a ratio of APB solids to sodium silicate solids between 0.03:1 and 0.5:1 and preferably 0.06:1 and 0.5:1. Therefore the suspension-solution using such a film-forming system would have the following composition. The total solids (film-forming + particulate) are 5.25 to 68%, the dissolved film-forming solids (APB + silicate) are 5.0 to 34.5% with 2.4 to 12% dissolved APB solids, and the suspended particulate solids are 0.25 to 51.2%. A system including sodium pentaborate (SPB) would have a ratio of SPB solids to sodium silicate between 0.02:1 and 0.3:1 and the suspension-solution would have the following composition. The total solids (film-forming + particulate) are 18.2 to 68%, the dissolved film-forming solids (SPB + silicate) are 17.4 to 34.5% with 6 to 7% SPB and the suspended particulate solids is 0.9 to 51.2%. A system with sodium hexametaphosphate (SHP) would have a ratio of SHP solids to sodium silicate solids between 1:1 and 3:1 and the suspension-solution would have the following composition. The total solids (film-forming + particulate) are 31 to 80%, the dissolved film-forming solids (SHP + silicate) are 29.6 to 48% and the suspended particulate solids are 1.5 to 60%.

후처리

customThe total solids (film-forming + particulate)

출처 및 근거

ORD 기록: ord-7a21c7382b7b43eca2ef5eba9b0401bc
출처 데이터셋: uspto-grants-1976_06
DOI: 10.6084/m9.figshare.5104873.v1
특허 번호: US03960583