Adipic Acid → Sodium silicate vinyl chloride propylene oxide

HRID 223427

반응식

HRID 223427 반응식
[Si:1]([O-:5])([O-:4])([O-:3])[O-:2].[Na+:6].[Na+].[Na+].[Na+].[CH2:10]1[O:13][CH:11]1[CH3:12].C(O)(=O)CCCCC(O)=O.C([O-])(=O)CCCCCCCCCCCCCCCCC.[Na+].C(OOC(=O)C1C=CC=CC=1)(=O)C1C=CC=CC=1.[CH:63]([Cl:65])=[CH2:64]>>[Si:1]([O-:5])([O-:4])([O-:3])[O-:2].[Na+:6].[Na+:6].[Na+:6].[Na+:6].[CH:63]([Cl:65])=[CH2:64].[CH2:10]1[O:13][CH:11]1[CH3:12]

참가 물질

7

반응물 6

HCID 196Adipic AcidHCID 6338Vinyl Chloride2회HCID 6378Propylene Oxide2회HCID 7187Benzoyl PeroxideHCID 26051Sodium orthosilicate2회HCID 2724691Sodium Stearate

생성물 1

HCID 86738391Sodium silicate vinyl chloride propylene oxide

반응 조건

온도
50 °C

실험 절차

About 50 parts by weight of an aqueous sodium silicate solution containing about 15% Na2O and 25% SiO2 by weight, 10 parts by weight of propylene oxide, 2 parts by weight of adipic acid, 0.2 parts by weight of sodium stearate and 0.1 part by weight of benzoyl peroxide are mixed then added to an autoclave and a temperature of about 50° C. is maintained at a pressure between 7.0 and 7.1 kg per cm2. Vinyl chloride monomer is slowly added while agitating over a period of 7 to 10 hours until the emulsion contains about 30% vinyl chloride polymerized with the sodium silicate and propylene oxide thereby producing an emulsion of poly(sodium silicate-vinyl chloride-propylene oxide) copolymer.

후처리

  1. additionare mixed
  2. additionthen added to an autoclave

출처 및 근거

ORD 기록
ord-6c0068f602ae41749e705c22f38e40f0