Calcium Chloride → Calcium Stearate

HRID 236886노트

반응식

HRID 236886 반응식
[Cl-].[Ca+2:2].[Cl-].[C:4]([O-:23])(=[O:22])[CH2:5][CH2:6][CH2:7][CH2:8][CH2:9][CH2:10][CH2:11][CH2:12][CH2:13][CH2:14][CH2:15][CH2:16][CH2:17][CH2:18][CH2:19][CH2:20][CH3:21].[NH4+]>O>[C:4]([O-:23])(=[O:22])[CH2:5][CH2:6][CH2:7][CH2:8][CH2:9][CH2:10][CH2:11][CH2:12][CH2:13][CH2:14][CH2:15][CH2:16][CH2:17][CH2:18][CH2:19][CH2:20][CH3:21].[Ca+2:2].[C:4]([O-:23])(=[O:22])[CH2:5][CH2:6][CH2:7][CH2:8][CH2:9][CH2:10][CH2:11][CH2:12][CH2:13][CH2:14][CH2:15][CH2:16][CH2:17][CH2:18][CH2:19][CH2:20][CH3:21]

참가 물질

4

반응물 2

HCID 5284359Calcium ChlorideHCID 9861187Ammonium Stearate

생성물 1

HCID 15324Calcium Stearate

시약·촉매·용매 1

HCID 962Water용매2회

실험 절차

272 ml. of water, 10 g. of Gelvatol 1-90 polyvinylalcohol and 5 g. of Acrysol WS-32 acrylic polymer were heated until the binders dissolved. 50 g. of stearic acid was then added and melted to form a liquid layer floating on the aqueous solution. 23 ml. of ammonium hyroxide (28% solution), which was the stoichiometric amount to form ammonium stearate, was then added dropwise to the gently stirred liquid. An intractable gel is formed which was transferred to a vigorously-stirred Waring Blendor, and then 20 g. of calcium chloride dissolved in 20 ml. of water slowly added until the mixture became solid. 50 ml. of water was then added with stirring until a creamy paste formed. After drying on a substrate this material gave a pressure-sensitive film with excellent hiding power. The formation of ammonium stearate in situ is the preferred method of preparation because it allows a higher solids content to be obtained and yields smaller particles of calcium stearate. The density of the dry coating was 0.5 g./cc which is equivalent to about 50% void volume.

후처리

  1. additionwas then added dropwise to the gently stirred liquid
  2. customAn intractable gel is formed which
  3. customformed
  4. customAfter drying on a substrate this material
  5. customgave a pressure-sensitive film with excellent hiding power
  6. customthe preferred method of preparation because it
  7. customto be obtained