1-Butanol → HCID 178514811, 화합물

The prepared substrate was next painted with a n-butanol solution containing salts of iridium and tantalum. The ratio of iridium to tantalum in the solution was approximately 65% to 35% by weight. The solution was allowed to dry at ambient temperature for approximately 20 minutes. The painted titanium substrate was subsequently heat treated in a furnace having an oxygen containing atmosphere at approximately 500° C. for approximately 20-30 minutes to form an iridium oxide/tantalum oxide composite coating. The process of painting and heat treating the titanium substrate was repeated in order to obtain a first layer having a total loading of approximately 2.0 g/m2. When the desired loading was achieved, the coated substrate was heat treated for approximately one hour at approximately 500° C.

1. customto dry at ambient temperature for approximately 20 minutes
2. temperatureThe painted titanium substrate was subsequently heat
3. additiontreated in a furnace
4. customat approximately 500° C.
5. customfor approximately 20-30 minutes

ORD 기록

ord-112b51fb4a4540469b0301fd066a7d32

출처 데이터셋

uspto-grants-2001_04

DOI

10.6084/m9.figshare.5104873.v1

특허 번호

US06217729B1