Acrylic Acid → Acrylic acid maleic acid

HRID 47191

반응식

HRID 47191 반응식
[C:1]([OH:8])(=[O:7])/[CH:2]=[CH:3]\[C:4]([OH:6])=[O:5].[OH-].[Na+].C(O)(=O)C=C.S(OOS([O-])(=O)=O)([O-])(=O)=O.[Na+].[Na+]>O>[C:4]([OH:6])(=[O:5])[CH:3]=[CH2:2].[C:1]([OH:8])(=[O:7])/[CH:2]=[CH:3]\[C:4]([OH:6])=[O:5]

참가 물질

6

반응물 4

HCID 6581Acrylic AcidHCID 14798Sodium HydroxideHCID 62655Sodium PersulfateHCID 444266Maleic Acid

생성물 1

HCID 86584291Acrylic acid maleic acid

시약·촉매·용매 1

HCID 962Water용매3회

반응 조건

온도
95 °C

실험 절차

11 g maleic acid was dissolved in 200 g deionized water, and this solution was adjusted to pH 3.85 with 48% aqueous sodium hydroxide. The mixture was heated to 95° C. and kept at 95 to 98° C. in nitrogen atmosphere, and 64 g acrylic acid dissolved in 16 g deionized water, and 4.7 g sodium persulfate dissolved in 50 g deionized water, were separately added dropwise thereto over the period of 2 hours. Thereafter, the reaction solution was kept at 98° C., stirred for 6 hours, and retuned to room temperature to give an aqueous solution of poly(acrylic acid/maleic acid). As a result of measurement of the resulting dispersant by GPC, the weight average molecular weight was 87,000 (determined using polyethylene glycol standards). The conditions for GPC measurement were the same as in Synthesis Example 1.

후처리

  1. customkept at 95 to 98° C. in nitrogen
  2. dissolutiondissolved in 16 g
  3. dissolutiondissolved in 50 g
  4. additionwere separately added dropwise
  5. customover the period of 2 hours
  6. customwas kept at 98° C.
  7. customretuned to room temperature