O.O.O=[Al]O[Si](O[Si](O[Al]=O)=O)=O.[P:14](=[O:18])([OH:17])([OH:16])[OH:15].[N+:19]([O-:22])([O-:21])=[O:20].[Ce+3:23].[N+]([O-])([O-])=O.[N+]([O-])([O-])=O.[C:32]([O-:37])(=[O:36])[C:33]([O-:35])=[O:34].[V+5:38].[C:39]([O-:44])(=[O:43])[C:40]([O-:42])=[O:41].[C:45]([O-:50])(=[O:49])[C:46]([O-:48])=[O:47].[C:51]([O-:56])(=[O:55])[C:52]([O-:54])=[O:53].[C:57]([O-:62])(=[O:61])[C:58]([O-:60])=[O:59].[V+5]>O>[P:14]([O-:18])([O-:17])([O-:16])=[O:15].[N+:19]([O-:22])([O-:21])=[O:20].[Ce+3:23].[N+:19]([O-:22])([O-:21])=[O:20].[N+:19]([O-:22])([O-:21])=[O:20].[C:32]([O-:37])(=[O:36])[C:33]([O-:35])=[O:34].[V+5:38].[C:39]([O-:44])(=[O:43])[C:40]([O-:42])=[O:41].[C:45]([O-:50])(=[O:49])[C:46]([O-:48])=[O:47].[C:51]([O-:56])(=[O:55])[C:52]([O-:54])=[O:53].[C:57]([O-:62])(=[O:61])[C:58]([O-:60])=[O:59].[V+5:38]

참가 물질

7

반응물 4

HCID 1004Phosphoric AcidHCID 24948Cerium nitrateHCID 56841936BentoneHCID 178526029HCID 178526029, 화합물

생성물 2

HCID 86755301Phosphate cerium nitrateHCID 178526029HCID 178526029, 화합물

시약·촉매·용매 1

HCID 962Water용매

실험 절차

A clay/phosphate/cerium nitrate, vanadium oxalate slurry was prepared by adding 1340 grams of Theile RC-320 kaolin clay slurry to 1795 milliliters of water in a high speed mixer. To this mixture, 192 grams of phosphoric acid was added. Thereafter, 431 grams of cerium nitrate solution and 232 grams of vanadium oxalate solution were added to the slurry. The slurry was then spray dried and then resulting particles were calcined at 650° C. for 30 minutes in a muffle furnace. The calcined particles were then mixed with magnesium oxide in a 50/50 weight percent ratio and analyzed by TGA tests. These tests indicated that the resulting material produced an SOx absorption of 0.27% per minute.

후처리

  1. customThe slurry was then spray dried
  2. additionThe calcined particles were then mixed with magnesium oxide in a 50/50 weight percent ratio
  3. customproduced
  4. customan SOx absorption of 0.27% per minute