Butyl Acrylate → 2-Propenoic acid, 2-methyl-, 2-oxiranylmethyl ester, polymer with butyl 2-propenoate

HRID 910568

반응식

HRID 910568 반응식
[C:1]([O:5][CH2:6][CH2:7][CH2:8][CH3:9])(=[O:4])[CH:2]=[CH2:3].[C:10]([O-:15])(=[O:14])[C:11]([CH3:13])=[CH2:12].N(C(C)(CC)C#N)=NC(C)(CC)C#N.[C:30]([O:33][CH2:34][CH3:35])(=O)C>C1(C)C=CC=CC=1>[CH2:6]([O:5][C:1](=[O:4])[CH:2]=[CH2:3])[CH2:7][CH2:8][CH3:9].[C:10]([O:15][CH2:35][CH:34]1[O:33][CH2:30]1)(=[O:14])[C:11]([CH3:13])=[CH2:12]

참가 물질

6

반응물 4

HCID 8846Butyl AcrylateHCID 8857Ethyl AcetateHCID 87595MethacrylateHCID 930792,2'-Azobis(2-methylbutyronitrile)

생성물 1

HCID 219157742-Propenoic acid, 2-methyl-, 2-oxiranylmethyl ester, polymer with butyl 2-propenoate

시약·촉매·용매 1

HCID 1140Toluene용매

반응 조건

온도
60 °C

실험 절차

The following were added to a 946 mL bottle: 72.0 g of butyl acrylate (Dow Chemical Co., Midland, Mich.), 48.0 g of glydicyl methacrylate (Sartomer Co. Inc., Easton, Pa.), 0.18 g of 2,2′-azobis(2-methylbutanenitrile) (DuPont, Wilmington, Del.), 140 g of ethyl acetate, and 140 g of toluene. The solution was purged with nitrogen for two minutes at a rate of one liter per minute. The bottle was sealed and placed in a water bath that was maintained at 60° C., for 24 hours. The reaction mixture was 29.5 wt % solids, had a measured inherent viscosity of 0.78 dL/g and a Brookfield viscosity of 0.7 Pascal-seconds.

후처리

  1. additionThe following were added to a 946 mL bottle
  2. customThe solution was purged with nitrogen for two minutes at a rate of one liter per minute
  3. customThe bottle was sealed
  4. customplaced in a water bath

출처 및 근거

ORD 기록
ord-5bdf334a565141ffa418479a92965abb
출처 데이터셋
uspto-grants-2011_09
특허 번호
US08022145B2

연결된 노트

불러오는 중…