tert-Butyl acrylate → p-Butoxystyrene t-butyl acrylate

HRID 962371

반응식

HRID 962371 반응식
[CH2:1]([O:5][C:6]1[CH:13]=[CH:12][C:9]([CH:10]=[CH2:11])=[CH:8][CH:7]=1)[CH2:2][CH2:3][CH3:4].[C:14]([O:18][C:19]([CH3:22])([CH3:21])[CH3:20])(=[O:17])[CH:15]=[CH2:16].C(OOC(CC)(CCCC)C([O-])=O)(C)(C)C>CC(C)=O>[CH2:1]([O:5][C:6]1[CH:7]=[CH:8][C:9]([CH:10]=[CH2:11])=[CH:12][CH:13]=1)[CH2:2][CH2:3][CH3:4].[C:14]([O:18][C:19]([CH3:22])([CH3:21])[CH3:20])(=[O:17])[CH:15]=[CH2:16]

참가 물질

5

반응물 3

HCID 15458tert-Butyl acrylateHCID 11715272p-ButoxystyreneHCID 22065482t-Butylperoxy(2-ethylhexanoate)

생성물 1

HCID 86752678p-Butoxystyrene t-butyl acrylate수율 70%

시약·촉매·용매 1

HCID 180Acetone용매

반응 조건

온도
90 °C

실험 절차

In an autoclave equipped with a 1.5-liter glass polymerization vessel and purged with nitrogen, polymerization reaction was carried out by dissolving 225.0 grams (1.28 mol) of p-butoxystyrene and 25.0 grams (0.20 mol) of t-butyl acrylate in 500 grams of acetone, adding 7.5 grams of t-butylperoxy(2-ethylhexanoate) as a polymerization catalyst, and heating the mixture at 90° C. Thereafter, the catalyst was added in incremental amounts, that is, 5.0 grams after 21/2 hours and 2.5 grams after 41/2 hours from the start of polymerization reaction. After 6 hours of polymerization, the reaction solution was cooled down and the acetone was distilled off. A 9/1 methanol/water mixture was added to the reaction solution, causing the copolymer to crystallize. The copolymer had a weight average molecular weight (Mw) of 9,200, a dispersity (Mw/Mn) of 1.64, and a copolymerization ratio of 6:1. The yield was 70.0%.

후처리

  1. custompurged with nitrogen, polymerization reaction
  2. additionThereafter, the catalyst was added in incremental amounts
  3. custom5.0 grams after 21/2 hours and 2.5 grams after 41/2 hours from the start of polymerization reaction
  4. customAfter 6 hours of polymerization
  5. temperaturethe reaction solution was cooled down
  6. distillationthe acetone was distilled off
  7. additionA 9/1 methanol/water mixture was added to the reaction solution
  8. customto crystallize