温度

70 °C

5 parts of ethylene-modified PVA (PVA-21) and 90 parts of ion-exchanged water were fed into a glass vessel equipped with a reflux condenser, a dropping funnel, a thermometer, a nitrogen inlet mouth and a stirrer, and completely dissolved at 95° C. Next, its pH was mad to be 4 with diluted sulfuric acid added there to, and then 10 parts of methyl methacrylate, 10 parts of n-butyl acrylate and 0.1 parts of n-dodecylmercaptan were added to it with stirring at 150 rpm. This was purged with nitrogen and heated up to 70° C. 5 parts of 1% potassium persulfate was added to it to start the polymerization. Then, a mixture of 40 parts of methyl methacrylate, 40 parts of n-butyl acrylate and 0.4 parts of n-dodecylmercaptan was continuously added to it, over a period of 2 hours. 3 hours after the start of the polymerization, the conversion reached 99.2%, and the polymerization was stopped in this stage. The process gave stable methyl methacrylate/n-butyl acrylate copolymer emulsion (Em-212) having a solid concentration of 51.5%.

1. customequipped with a reflux condenser, a dropping funnel
2. dissolutiona thermometer, a nitrogen inlet mouth and a stirrer, and completely dissolved at 95° C
3. additionwere added to it
4. customThis was purged with nitrogen
5. addition5 parts of 1% potassium persulfate was added to it
6. customthe polymerization
7. additionwas continuously added to it, over a period of 2 hours
8. custom3 hours after the start of the polymerization