Acrylonitrile → Acrylonitrile alpha-methylstyrene

A one-gallon, glass-lined latex reactor was charged with 1691 g of deionized water, 107 g of polystyrene seed latex (400 Angstrom number average particle size) (30% active), 0.2 g of disodium ethylene diaminetetraacetic acid, 1.0 g of sodium bicarbonate, and 20 g of 43% aqueous sodium n-dodecylbenzene sulfonate. The mixture was purged with nitrogen, and the reactor was then evacuated with a water aspirator three times at room temperature. After the final evacuation, the reactor was pressurized with 10 psi (69 KPa) of nitrogen. The reactor was heated to 85° C. and stirred at 150 rpm. An aqueous feed consisting of 154 g of water, 27.7 g of 43% aqueous sodium n-dodecylbenzene sulfonate, and 2.7 g of sodium persulfate and a monomer feed consisting of 750 g of α-methylstyrene, 187.5 g of acrylonitrile, (providing a ratio α-methylstyrene/acrylonitrile of 80/20) and 0.68 g of n-octyl mercaptan (first monomer feed stream) were started simultaneously and added at rates of 37.4 and 234.6 g per hour to the reaction, respectively. After four hours, addition of first monomer feed stream was halted and the second monomer feed stream consisting of 41.4 g of acrylonitrile and 0.53 g of n-octyl mercaptan was started at a rate of 20.7 g per hour. The aqueous feed rate was changed to 15.5 g per hour. The additions of aqueous feed and second monomer stream were continued for three additional hours. Total monomer feed resulted in a ratio, α-methylstyrene/acrylonitrile, of 77/23. The second monomer feed was then halted, the aqueous feed continued for an additional 15 minutes, and the mixture was retained at 85° C. for 15 minutes. An antifoaming agent (antifoam H-10, 15% active, available from Dow Corning Corporation) was added and volatile components were steam distilled from the mixture. The reaction went to 92% conversion.

1. additionaddition of first monomer feed stream

ORD record

ord-08e56c90ce6d485e82d0e3efb4a84d14

Source dataset

uspto-grants-1990_11

DOI

10.6084/m9.figshare.5104873.v1

Patent number

US04972032