An aqueous solution in which 4.16 kg of aluminum nitrate nonahydrate and 540 g of 60% nitric acid were dissolved in 5.0 L of pure water was gradually dropped into 20.0 kg of a stirred silica sol solution having a colloidal particle diameter of from 10 to 20 nm held at 15° C. (Snowtex N-30 manufactured by Nissan Chemical Industries, Ltd. (SiO2 content: 30% by mass)) to obtain a mixed slurry of silica sol and aluminum nitrate. Subsequently, the mixed slurry was aged by holding at 50° C. for 24 hours. After cooling to room temperature, the mixed slurry was spray-dried with a spray dryer set to an outlet temperature of 130° C. to obtain a solid.