反应详情

Into a 500 ml-volume three-neck flask, 57.0 g (0.36 mol) of 2-tetrahydropyranyl methacrylate, 31.7 g (0.18 mol) of p-vinylphenyl glycidyl ether, 7.8 g (0.06 mol) of 2-hydroxyethyl methacrylate and 300 ml of methyl isobutyl ketone were charged. A catalytic amount of 2,2′-azobis(methyl 2-methylpropionate) was added thereto as a radical polymerization initiator, and polymerization was allowed to proceed at 80° C. for 6 hours in a nitrogen stream. The reaction solution was cooled and then poured in a large amount of heptane to precipitate a polymer. The crystal was collected by filtration and dissolved in diethylene glycol ethyl methyl ether, and heptane and methyl isobutyl ketone contained in the solution were removed by distillation under reduced pressure to obtain Polymer A-6 (2-tetrahydropyranyl methacrylate/p-vinylphenyl glycidyl ether/2-hydroxyethyl methacrylate) as a diethylene glycol ethyl methyl ether solution.

1. customas a radical polymerization initiator, and polymerization
2. temperatureThe reaction solution was cooled
3. customto precipitate a polymer
4. filtrationThe crystal was collected by filtration
5. dissolutiondissolved in diethylene glycol ethyl methyl ether
6. customwere removed by distillation under reduced pressure