Methanol → 2-Hydroxyethyl Methacrylate

To a stirred solution of 1.74 g (2 ml, 10 mmoles) of MTS and 1 ml of 1 M tris(dimethylamino)sulfonium difluorotrimethylsilicate/acetonitrile in 20 ml of anhydrous THF under argon was added dropwise a mixture of 5 g (50 mmoles) of MMA and 10.1 g (50 mmoles) of 2-trimethylsiloxyethyl methacrylate (prepared by the reaction of chlorotrimethylsilane with 2-hydroxyethyl methacrylate in the presence of triethylamine). Exothermic copolymerization occurred. After stirring for 1 h at ambient temperature, 10 ml of methanol was added, and the solution was refluxed for 1 h. Evaporation in vacuo gave 12.79 g of copolymer, the NMR spectrum of which showed it to contain 11% of the residual trimethylsilyl protecting group due to incomplete methanolysis. To complete methanolysis, 6 g of the copolymer was stirred at reflux for 1 h with 20 ml of methanol, 20 ml of THF and 1 ml of 1 M tetrabutylammonium fluoride/THF. Evaporation of the solution in vacuo gave 5.6 g of poly(MMA/2-hydroxyethyl methacrylate) copolymer. GPC: Mn 1400, Mw 1500, D 1.07 (theor. M.W. 1150). 220 MHz NMR: 1:1 mole ratio of MMA and hydroxyethyl methacrylate. Hydroxyl number: 233, 246 (equivalent to 49 mole % hydroxyethyl methacrylate polymer repeat units and 51 mole % MMA polymer repeat units.

1. customEvaporation of the solution in vacuo

ORD record

ord-89faa07fec15448689588c39b6d1e6c8

Source dataset

uspto-grants-1983_11

DOI

10.6084/m9.figshare.5104873.v1

Patent number

US04414372