反应详情

温度

50 °C

Sodium chloride (116 g), 4 drops concentrated sulfuric acid and 150 g of water are added to a 1-liter flask containing an efficient two-tiered stirrer, condenser, and nitrogen inlet tube. Polyacrylic acid dispersant, such as 5 gm of Primafloc C-7 available from Rohm and Haas Company, is then added to a solution containing a 0.1 g tannic acid dissolved in 136 g of water. This solution is then added to the stirred flask containing sodium chloride. This aqueous phase is then sparged with nitrogen. In a separate flask, 314 mls. of acrolein is sparged for 20 - 30 minutes with nitrogen. In a separate flask a solution of 29.6 g of divinylbenzene (DVB-81.1% active), 6.0 g of diethyleneglycoldivinylether (DEGDVE), and 9.0 g of Percadox 16 (bis-t-butylcyclohexyl percarbonate) is prepared. This latter solution is then added to acrolein, shaken until homogeneous, and added to the aqueous phase in the reaction flask after the stirrer had been turned off and the nitrogen sparge had been converted to a nitrogen atmosphere. A suspension formed in 20 - 30 minutes on intermittent agitation at 145 rpm. The position of the stirrer blade must be at the interfaces of the two liquid phases. After the dispersion is formed, the reaction mixture is heated to 50°C. and held there with intermittent heating and air cooling for 16 hours. The reaction contents are then cooled to room temperature, the liquid drained, and the resin given three water washes. After washing with methanol, the resin is dried at 75°C. for 16 hours.

1. additioncontaining an efficient two-tiered stirrer, condenser, and nitrogen inlet tube
2. additionThis solution is then added to the stirred flask
3. customThis aqueous phase is then sparged with nitrogen
4. customof acrolein is sparged for 20 - 30 minutes with nitrogen
5. additionadded to the aqueous phase in the reaction flask after the stirrer
6. customthe nitrogen sparge
7. customA suspension formed in 20 - 30 minutes on intermittent agitation at 145 rpm
8. customAfter the dispersion is formed
9. temperaturewith intermittent heating
10. temperatureair cooling for 16 hours
11. customThe reaction contents
12. temperatureare then cooled to room temperature
13. washAfter washing with methanol
14. customthe resin is dried at 75°C. for 16 hours