Methacrylic Acid → HCID 86588648, compound

HRID 1823705Notes

Reaction equation

[C:1]([OH:6])(=[O:5])[C:2]([CH3:4])=[CH2:3].[C:7]([O:12][CH2:13][CH:14]=[CH2:15])(=[O:11])[C:8]([CH3:10])=[CH2:9].[C:16]([O:21][CH:22]1[CH2:27][CH2:26][CH2:25][CH2:24][CH2:23]1)(=[O:20])[C:17]([CH3:19])=[CH2:18].N(C(C)(CC(C)C)C#N)=NC(C)(CC(C)C)C#N>COCC(OC(=O)C)C>[C:1]([OH:6])(=[O:5])[C:2]([CH3:4])=[CH2:3].[C:7]([O:12][CH2:13][CH:14]=[CH2:15])(=[O:11])[C:8]([CH3:10])=[CH2:9].[C:16]([O:21][CH:22]1[CH2:27][CH2:26][CH2:25][CH2:24][CH2:23]1)(=[O:20])[C:17]([CH3:19])=[CH2:18]

Participants

Conditions

Temperature: 70 °C

Procedure

803 parts of 1-methoxy-2-acetoxypropane were charged in a reaction vessel and heated under a nitrogen flow so that the internal temperature of the vessel was 70° C. Then a solution in which 54.0 parts of methacrylic acid, 135.6 parts of allyl methacrylate, 90.4 parts of cyclohexyl methacrylate (composition ratio of these methacrylic acid and esters thereof was 28:48:24 in molar ratio), 4.53 parts of dodecylmercaptane and 11.1 parts of V-65 (2,2′-azobis-(2,4′-dimethylvaleronitrile), manufactured by Wako Pure Chemical Co.) were dissolved in 803 parts of 1-methoxy-2-acetoxypropane was dropwise added into the vessel over a period of 2.5 hours. The mixture was agitated further for 2 hours under heating at 70° C. to obtain a methacrylic acid/allyl methacrylate/cyclohexyl methacrylate terpolymer (terpolymer 2). The weight-average molecular weight of the terpolymer was 36,000 (converted as polystyrene).

Workup

temperatureheated under a nitrogen flow so that the internal temperature of the vessel
customwas 70° C
additionwas dropwise added into the vessel over a period of 2.5 hours

Sources & evidence

ORD record: ord-d296b42032b344fe9cd232a8d368d34c
Source dataset: uspto-grants-2006_05
DOI: 10.6084/m9.figshare.5104873.v1
Patent number: US07041416B2

Reaction notes

Loading…