150 parts of acetone, 71.1 parts of vinyl chloride, 28.9 parts of lauryl methacrylate and 1.5 parts of benzoyl peroxide were charged to an autoclave and heated to 51° C. for 154 hours. The resulting slurry was washed thoroughly with isopropanol, centrifuged and dried for 64 hours at 30° C. and 2.0 mm. Hg. There was obtained a lauryl methacrylate/vinyl chloride copolymer interfacial agent (about 90% conversion) product. Said interfacial agent was a dry white powder and had a reduced viscosity of 0.29 dl./g. as measured on a solution of 0.2 grams in 100 ml. of benzene at 30° C.