70 parts by weight of alpha-methylstyrene, 30 parts by weight of acrylonitrile, 5 parts by weight of toluene, 0.135 parts by weight of 1,1-bis (tert-butylperoxi)-3,3,5 trimethylcyclohexane and 0.015 parts by weight of di-tert-butyl peroxide were homogenously mixed and continuously introduced to the reactor. The polymerization was carried out as the reaction temperature was kept at 110° C. After completion of the polymerization, the resulting polymer was supplied to a vaporizer equipped with a heat exchanger, kept at a temperature of 250° C. and a pressure of 20 Torr, in which non-reacted monomers and solvents were removed. Then, the polymer was palletized through an extruder equipped with a discharge pump. The alpha-methylstyrene-acrylonitrile copolymer prepared by the above method had an average molecular weight of 9.5×104 and a glass transition temperature (Tg) of 125° C.

1. additioncontinuously introduced to the reactor
2. customwas kept at 110° C
3. customAfter completion of the polymerization
4. customequipped with a heat exchanger
5. customkept at a temperature of 250° C.
6. customa pressure of 20 Torr, in which non-reacted monomers and solvents were removed
7. customequipped with a discharge pump
8. customThe alpha-methylstyrene-acrylonitrile copolymer prepared by the above method
9. customa glass transition temperature (Tg) of 125° C.