A solution of 106.4 grams (0.95 mole) 1-octene and 5.5 grams (0.0509 mole) 1,7-octadiene (molar charge ratio 95:5) in 450 grams of heptane was polymerized with Et2AlCl (16 millimoles) and AATiCl3 (4.0 millimoles) at 50° C. for 10 hours. During the course of the reaction, hydrogen was bubbled through the reaction mixture. The conversion of the polymer was 65 percent, inherent viscosity was 2.1 dl/gram. The composition of monomers in the copolymer was 97:3 mole ratio from NMR analysis.