反应详情

温度

95 °C

A zinc acrylate polymer was prepared by the reaction of zinc oxide and naphthenic acid (acid value 200 mgKOH/g) with a carboxylic acid functional acrylic copolymer based on the monomers; Acrylic acid (16.8 mol %)/Ethyl acrylate (73.5 mol %), methoxy polyethyleneglycol methacrylate (MPEG350) (1.3 mol %) and cyclohexyl methacrylate (8.4 mol %). These components were mixed at a 1:1:1 molar ratio (zinc oxide:naphthenic acid:polymer carboxylic acid groups) in xylene/n-butanol (4:1 weight ratio) and heated and stirred at 95° C. until a clear solution was obtained resulting in a solution of zinc acrylate polymer of 48.6 wt % in xylene/n-butanol/water (41.2:9.3:0.9 wt %).

1. additionThese components were mixed at a 1:1
2. customwas obtained