反应详情

102 kg (approximately 400 moles) of 2,4-dicyanoglutaric acid diethyl ester (approximately 94%) were mixed with 20 kg of water in a 400 liter capacity stirrer-equipped vessel, followed by the addition of 8.5 kg (261 moles) of polyoxymethylene (92%). To adjust to a pH-value of from 4 to 6, 383 g of a 32% NaOH solution (corresponding to 3.08 moles) were added. The reaction was carried out with stirring at a temperature of from 80° C. to 130° C. under the pressure spontaneously built up in the closed vessel. The reaction time was 45 minutes. The added water and the water of reaction were distilled off in a steam jet vacuum. The resulting condensation product was then subjected to thermolysis for 120 minutes at a temperature of from 150° C. to 180° C. under a pressure of less than 1 bar. To prevent polymerization, SO2 gas was passed through the thermolysis reaction mixture and through the distillate in the following distillation step. Distillation of the crude product formed during thermolysis produced 48.6 kg (389 moles) of 2-cyanoacrylic acid ethyl ester. This yield was 51% by weight, based on the dicyanoglutarate used.

1. customstirrer-equipped vessel
2. additionwere added
3. distillationwere distilled off in a steam jet vacuum
4. customThe resulting condensation product
5. customfor 120 minutes
6. customof from 150° C. to 180° C.
7. custompolymerization, SO2 gas
8. customwas passed through the thermolysis reaction mixture and through the distillate in the following distillation step
9. distillationDistillation of the crude product