A mixture of methyl acrylate, monoethyl maleate, and benzene (weight ratio: 68.28/2.46/29.26) was pressured to about 422 kg./sq. cm.; ethylene was separately pressured to about 422 kg./sq. cm. Separate streams of this mixture (0.91 kg./hr.) and ethylene (6.35 kg./hr.) were joined and pressured to 1900 kg./sq. cm. The resulting feed stream then entered the autoclave. Simultaneously, a catalyst solution, made by adding 50 ml. of tert-butyl peroxypivalate to 4.5 kg. of benzene was introduced at the rate of 0.00204 kg./hr. to keep the temperature at 170° C. The effluent from the autoclave passed through a let-down valve to a chamber at atmospheric pressure where most of the residual monomers and solvent flashed off. The ethylene/methyl acrylate/monoethyl maleate terpolymer thus isolated was freed from the small amount of residual volatiles by heating for 16 hours at 80° C. in a nitrogen stream. Acid-base titration indicated that 0.25 meq. of acid groups was present per gram of terpolymer. This corresponds to 3.6 weight percent of monoethyl ester of maleic acid.

1. additionby adding 50 ml
2. customat 170° C
3. customThe effluent from the autoclave passed through a let-down valve to a chamber at atmospheric pressure where most of the residual monomers and solvent