反应详情

温度

60 °C

A Cu containing catalyst was prepared by ion-exchange with copper acetate. A 0.3 M copper (II) acetate monohydrate solution was prepared by dissolving 96 g of the copper salt in 1.6 L of deionized water at 60° C. 300 g of the calcined zeolite of example 1 was then added to this solution. An ion-exchange reaction between the H-form of the calcined zeolite described in example 1 and the copper ions was carried out by agitating the slurry at 60° C. for 1 hour. The pH was between 4.5 and 4.8 during the reaction. The resulting mixture was then filtered, washed until the filtrate had a conductivity of <200 μScm−1, which indicated that substantially no soluble or free copper remained in the sample, and the washed sample was dried at 90° C. The obtained Cu catalyst comprised CuO at 3.29% by weight and Na at 300 ppm, both reported on a volatile free basis. The BET surface of the calcined material was 468 m2/g, determined according to DIN 66131, and the Langmuir surface area was 636 m2/g, determined according to DIN 66135.

1. customThe pH was between 4.5 and 4.8 during the reaction
2. filtrationThe resulting mixture was then filtered
3. washwashed until the filtrate
4. customthe washed sample was dried at 90° C