644 g of a silicon nitride powder (SN-E10 manufactured by Ube Industries, Ltd.; average particle size: 0.3 μm), 276 g of a silicon carbide (beta random ultrafine grade manufactured by Ibiden Co., Ltd.; average particle size: 0.27 μm), 80 g of an yttrium oxide powder (manufactured by Nippon Yttrium Co., Ltd.; average particle size: 1.4 μm) and 1000 g of ethanol as the dispersion medium were blended under pulverizing in a ball mill for 18 hours using 800 g of silicon nitride balls as a tumbling media. The resultant mixture was dried to obtain a starting ceramic powder mixture having a BET specific surface area of 12.1 m2 /g. The above amounts, 644 g of silicon nitride and 276 g of silicon carbide, correspond to theoretical amounts of silicon nitride and silicon carbide formed from 578.6 g of silicon and 82.9 g of carbon black used in Example 1.

1. dry with materialThe resultant mixture was dried
2. customto obtain a starting ceramic powder mixture