反应详情

温度

135 °C

About 525.0 grams (4.73 equiv.) of isophorone diisocyanate1 and 1.5 grams of dibutyltindilaurate2 catalyst, followed by 986 grams (3.88 equiv.) of octylphenol ethoxylate3, were added to a 3000 ml three-neck resin kettle equipped with a Trubore stirrer, N2 atmosphere inlet, and a thermocouple-temperature controller. The reaction mixture was heated to about 135° C., about 346.1 grams (0.497 equiv.) of a yellow polymeric colorant corresponding to Colorant A from Table I of U.S. Pat. No. 5,231,135 were added and the reaction mixture was heated for approximately 2 hours. An additional about 110.0 grams (0.433 equiv.) of octylphenol ethoxylate3 were added and the reaction mixture was heated at about 150° C. for approximately 2 hours. An FT-IR of the product was obtained to insure all of the isocyanate (NCO) functionality was consumed. The absence (disappearance) of a peak at about 2285 cm−1 (NCO) and the appearance (or increase in magnitude) of peaks at about 1740-1680 cm−1 and about 1540-1530 cm−1 corresponding to urethane frequencies were used to confirm this. The diurethane reaction product was poured into aluminum molds and allowed to cool and harden. This final colored resin product was characterized by the following physical properties: viscosity of about 121 cPs as measured by a Ferranti-Shirley cone-plate viscometer at about 140° C., a melting point of about 38° C. to about 115° C. as measured by electrothermal capillary melting point apparatus, a Tg of about 12.4° C. as measured by differential scanning calorimetry using a DuPont 2100 calorimeter at a scan rate of 20° C./minute, and a spectral strength of about 5634 milliliters Absorbance Units per gram at λmax as measured by dilution in n-butanol using a Perkin Elmer Lambda 2S UV/VIS spectrophotometer.

1. additionwere added to a 3000 ml three-neck resin kettle
2. addition5,231,135 were added
3. temperaturethe reaction mixture was heated for approximately 2 hours
4. temperaturethe reaction mixture was heated at about 150° C. for approximately 2 hours
5. customAn FT-IR of the product was obtained
6. customwas consumed
7. temperatureThe absence (disappearance) of a peak at about 2285 cm−1 (NCO) and the appearance (or increase in magnitude) of peaks at about 1740-1680 cm−1 and about 1540-1530 cm−1 corresponding to urethane frequencies
8. customThe diurethane reaction product
9. temperatureto cool
10. customas measured by a Ferranti-Shirley cone-plate viscometer at about 140° C.