HRID40173

反应详情

EQUATION

反应方程式

REACTANTS

反应物

HCID6658

Methyl methacrylate

C5H8O2

2 次

HCID7900

1-Methoxy-2-propanol

C4H10O2

HCID31256

Diacetone alcohol

C6H12O2

结构：CCC(C)(C)c1cc(-n2nc3ccccc3n2)c(O)c(C(C)(C)CC)c1

HCID33263

2-(2-Hydroxy-3,5-di-tert-pentylphenyl)benzotriazole

C22H29N3O

2 次

结构：CC(C)(C)CC(C)(C)c1ccc(O)c(-n2nc3ccccc3n2)c1

HCID62485

Octrizole

C20H25N3O

2 次

结构：CCCCCCCCOC(=O)CCc1cc(-n2nc3ccccc3n2)c(O)c(C(C)(C)C)c1

HCID9868461

Octyl 3-[3-(2H-benzotriazol-2-yl)-5-tert-butyl-4-hydroxyphenyl]propanoate

C27H37N3O3

2 次

PRODUCTS

生成物

HCID178418385

未命名化合物

PROCEDURE

实验过程

A coating solution was prepared containing 7 grams (g) of Elvacite 2041 PMMA, 79 g of 1-methoxy-2-propanol, 14 g of diacetone alcohol, 0.85 g of Tinuvin 384, 0.43 g of Tinuvin 328, 0.22 g of Cyasorb 5411, and 2 drops of BYK 331 surfactant. Thus, the solution contains 7% PMMA by total weight and 10% Tinuvin 384, 5% Tinuvin 328, and 2.5% Cyasorb 5411 based on solids. This solution was applied by flow coating onto 7 mil (177.8 μm) polycarbonate films 10 inches (25.4 cm) wide and 15 inches (38.1 cm) long, the solvent was flashed at 50° C. for 10 minutes, and the coated film was baked for 1 hour at 100° C. The top 5 inches (12.7 cm) of the films was discarded.

WORKUP

后处理

customA coating solution was prepared
waitthe coated film was baked for 1 hour at 100° C