反应详情

温度

60 °C

In 59.69 g of methanol were dissolved 18.52 g (68.77 mmol) of 11-methacrylamidoundecanoic acid (MAU), 1.48 g (7.64 mmol) of N,N-dimethylaminoethyl acrylate methyl chloride (Kohjin Co., Ltd.), and 0.31 g (1.89 mmol) of azobisisobutyronitrile (Nacalai Tesque, Inc.). The solution was deaerated by bubbling nitrogen for 60 minutes. The container was covered with a septum, and the polymerization was conducted by heating at 60° C. for 20 hours. After the completion of the polymerization reaction, the obtained solution was dropwise added into a large excess of acetone, and the resulting precipitate was collected by filtration under suction. After drying under reduced pressure, 9.43 g of random MAU/N,N-dimethylaminoethyl acrylate methyl chloride copolymer (90/10) was obtained (yield: 47.2%). The weight average molecular weight was 68000.

1. customby bubbling nitrogen for 60 minutes
2. customAfter the completion of the polymerization reaction
3. filtrationthe resulting precipitate was collected by filtration under suction
4. customAfter drying under reduced pressure