In 59.69 g of methanol were dissolved 18.43 g (68.43 mmol) of 11-methacrylamidoundecanoic acid (MAU), 1.57 g (7.60 mmol) of N,N-dimethylaminopropylacrylamide methyl chloride (Kohjin Co., Ltd.), and 0.31 g (1.89 mmol) of azobisisobutyronitrile (Nacalai Tesque, Inc.). The solution was deaerated by bubbling nitrogen for 60 minutes. The container was covered with a septum, and the polymerization was conducted by heating at 60° C. for 20 hours. After the completion of the polymerization reaction, the obtained solution was dropwise added into a large excess of acetone, and the resulting precipitate was collected by filtration under suction. After drying under reduced pressure, 9.60 g of random MAU/N,N-dimethylaminopropylacrylamide methyl chloride copolymer (90/10) was obtained (yield: 48.0%). The weight average molecular weight was 42000.

1. customby bubbling nitrogen for 60 minutes
2. customAfter the completion of the polymerization reaction
3. filtrationthe resulting precipitate was collected by filtration under suction
4. customAfter drying under reduced pressure