To a 500 ml resin kettle equipped with a mechanical stirrer, thermometer, pressure compensated addition funnel, and reflux condenser, was added hydroxypropylacrylate (26.6 g; 0.2 mole). Isopropenyl phosphonic acid (25.4 g; 0.2 mole) was dissolved in 154.2 g water and added rapidly to the kettle. The reaction mixture was then sparged with nitrogen for 1/2 hour. Ammonium persulfate (6 g) was added and the nitrogen sparge continued for an additional 1/2 hour. The mixture was heated to reflux for 2 hours. An additional 6 g of ammonium persulfate was added. The mixture was then refluxed for an additional 2 hours. There was a definite increase in viscosity after the second addition of ammonium persulfate. The yellow product had a pH of 1.00 and was tested without further purification. A 31PMR spectrum showed broad polymer absorptions centered at δ=-32.9 and -34.7 ppm and a small amount of monomer at δ=-19.0 ppm. There was also a trace of inorganic phosphate.

1. additionaddition funnel
2. temperaturereflux condenser
3. additionadded rapidly to the kettle
4. customThe reaction mixture was then sparged with nitrogen for 1/2 hour
5. additionAmmonium persulfate (6 g) was added
6. customthe nitrogen sparge
7. temperatureThe mixture was heated
8. temperatureto reflux for 2 hours
9. additionAn additional 6 g of ammonium persulfate was added
10. temperatureThe mixture was then refluxed for an additional 2 hours
11. temperaturea definite increase in viscosity
12. additionafter the second addition of ammonium persulfate
13. customwas tested without further purification