A synthesis was conducted by the same procedure as in the resin 1 except that n-butyl acrylate (nBA) and acrylic acid (AA) were used as monomers, thereby obtaining an nBA-AA type resin 3. The resin 3 was neutralized with an aqueous solution of potassium hydroxide to obtain an aqueous solution having a solid content concentration of 20% by mass. Incidentally, the resin 3 was in a state dissolved in the aqueous solution, and so the 50% cumulative volume average particle size (D50) of the resin 3 could not be measured. The weight average molecular weight of the resin 3 in terms of polystyrene was 9,000. The glass transition temperature of the resin 3 was 20° C. The acid value of the resin 3 as measured by a neutralization titration method was 260 mg KOH/g.